Thermoplastic Acrylic Resins

Product Tg C Color Gardner Viscosity Slovent Solids Recommended Usage Area TDS
TPA 22W/60 22 < 1 Z1 - Z3 white spirit 60% Masonry paints for interior use and plaster primer  Download
TPA 60X/60 60 < 1 Z5 - Z7 xylene 60% aerosol spray paintings utilizing N Hexane  Download
TPA 64X/55 64 < 1 Z5 +- xylene 55% plastic and metal top coats  Download
TPA 77X/60 77 < 1 Z7 +- xylene 60% exterior or interior sealer /masonry paint/ traffic paints  Download
TPA 44X/58 44 < 1 Z7 +- xylene 58% exterior or interior sealer /masonry paint/ traffic paints  Download

 

Acrylic Polyol Resins

Product OH % on solids Color Gardner Viscosity Slovent Solids Recommended Usage Area TDS
OHA 10S/50 1 < 1 Z3 - Z5 MIXED 50% General purpose 2K polyurethane clear or pigmented wood finishes.  Download
OHA 11S/60 1.1 < 1 Z4 - Z6 MIXED 60% Economical 2K polyurethane clear or pigmented wood finishes  Download
OHA 110S/60 1.1 < 1 Z4 - Z6 MIXED 60% "Economical 2K polyurethane clear or pigmented wood finishes. Cellulose Acetate Butyrate (CAB) compatibility"  Download
OHA 12SN/60 1.2 < 1 Z1 - Z3 SOLVENT NAPHTHA 60% Low isocyanate demand resin with good exterior durability.  Download
OHA 12SN/70 1.2 < 1 Z3 - Z5 SOLVENT NAPHTHA 70% Low isocyanate demand resin with good exterior durability.  Download
OHA 125SN/60 1.25 < 1 Z2 - Z3 SOLVENT NAPHTHA 60% Low isocyanate demand resin with good exterior durability.  Download
OHA 180S/60 1.8 < 1 Z3 - Z4 MIXED 60% "General purpose 2K polyurethanes requiring Cellulose Acetate Butyrate (CAB) compatibility."  Download
OHA 24SN/60 2.6 < 1 X - Z SOLVENT NAPHTHA 60% "General purpose 2K polyurethane for architectural and metal topcoats."  Download
OHA 270X/60 2.7 < 1 Y - Z1 XYLENE 60% "General purpose 2K polyurethane coatings with good durability, hardness and chemical resistance"  Download

 


About us

contact us

Plot 4, Street 7, Block 47, West Shuaiba Industrial Area, Mina Abdullah Industrial Area - Kuwait
Postal Address : 26011 Safat , 13121 Kuwait
(+965) 23263297
(+965) 23260179
info@uopkt.com